ASTM A213 Steel Pipe
-
Payment
-
Origin
China Mainland
-
Minimum Order
1
-
Packing
Pieces
- Contact Now Start Order
- Description
Product Detail
Cold finished and stress-relieved annealing BKS(+SR)
Annealed GBK(+A)
Normalized NBK(+N)
ASTM A213 is a standard of American Society of Testing Materials, it is for Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes.
Product Name | T11 steel pipe | T12 steel pipe | T91 steel pipe | T92 steel pipe |
chemical analysis | C:0.05-0.15;Si: 0.50-1.00;Mn:0.30-0.60;P: 0.025; S: 0.025;Cr:1.00-1.50;Mo:0.44-0.65 | C:0.05-0.15;Si: 0.50;Mn:0.30-0.61;P: 0.025; S: 0.025;Cr:0.80-1.25;Mo:0.44-0.65 | C:0.08-0.12;Si:0.20-0.50;Mn:0.30-0.60;P: 0.02; S: 0.01;Cr: 8.00-9.50;Mo:0.85-1.05 | C:0.07-0.13;Si: 0.50;Mn:0.30-0.60;P: 0.020; S: 0.010;Cr:8.50-9.50;Mo:0.30-0.60 |
Tensile Strength | - | 415 | 585 | 620 |
Yield strength | - | 220 | 415 | 440 |
Standard | ASTM A213 | |||
Length | As customer s request | |||
Packaging | Standard export packing, packed in woven bags, with two nylon slings, or can be customized as request | |||
Heat Treatment/ Delivery Condition | Heat treatment is applied following the last cold forming process. Subject to appropriate processing conditions, the increase in the residual stresses involved enables both forming and machining to a certain degree. The last Cold forming process is followed by annealing in a controlled atmosphere. The last cold forming process is followed by annealing above the upper transformation point in a controlled atmosphere. | |||
Delivery Time | Within 35-50 days from receiving deposit | |||
Payment Term | 100% L/C at sight or 30% deposit, 70% balance against copy of B/L | |||
Usage/Application | Pipes for boiler and superheater | |||
Main Market | Asia, Middle East, Europe, etc. |